The graphitization behavior of ultrahigh carbon steels containing Si in hot rolling processes was investigated. The graphite stringers went mostly through the small pores and generally paralleled to the rolling direction. The influence of alloy elements on graphitization was estimated based on thermodynamics, which showed that Si content was important for graphitization. Graphite stringers nucleated at small pores and grew with carbon diffusion during hot rolling. Alloy contents, pores and hot deformation at γ+Fe3C phase range were the key factors for the formation of graphite. The probable effect of deformation on graphite formation during hot rolling was discussed in this paper.
关键词:
Graphitization
,
null
,
null
,
null
Guangmin LUO
,
Jiansheng WU
,
Qingsen MENG
材料科学技术（英）
T91 steel is one of the new materials presently employed in power plant pipe components. The creep rupture strength and microstructure of the T91+10CrMo910 and T91+13CrMo44 welded joints were analyzed during creep rupture tests. Creep transgranular ductile rupture occurred at the 10CrMo910 matrix in the T91+10CrMo910 welded joints and creep intergranular brittle rupture occurred at the 13CrMo44 HAZ in the T91+13CrMo44 joints. Microhardness measurements showed high hardness at the heat affected zone (HAZ) of T91 and a sharply drop at the 13CrMo44 HAZ during creep rupture. The metallographic tests showed that no obvious microstructure degradation was observed in the 10CrMo910 HAZ and matrix, while creep cracks appeared at the 13CrMo44 HAZ. T91 steel had relatively high creep resistant strength in the welded joints tested. Recovery occurred in the T91 HAZ with the growth of subgrain size and the decrease of dislocation density during creep. It was concluded that the dissimilar joints of T91 and low alloy heat-resistant steel should have close creep strength matching to increase the service life of the overall joints at elevated temperature.
关键词:
T91 steel
,
null
,
null